RA 446
446 has a high ductile-to-brittle impact transition temperature. Therefore, successful forming and bending is aided by low forming speeds, edge preparation and preheating to 250-400°F. Annealing, when necessary should be performed at 1550-1650°F followed by rapid cool.
Welding may be accomplished by conventional methods. Preheating and postheating to 300-600°F is helpful. Austenitic weld fillers, such as AWS E310 or E312 are generally suggested to maximize weld deposit ductility.