Sandmeyer Nickel Alloy 800HT
Alloy 800H has good creeprupture properties at temperatures above 1100°F (600°C). It remains ductile during long term use at temperatures below 1290°F (700°C) due to a maximum titanium and aluminum content of 0.7%. Alloy 800 with a standard anneal is recommended for service below 1100°F (600°C). Alloy 800H resists reducing, oxidizing and nitriding atmospheres, as well as, atmospheres that alternate between reducing and oxidizing. The alloy remains stable in long term high temperature service.
Alloy 800HT has excellent creep strength at temperatures above 1290°F (700°C). If the application involves frequent temperature excursions under 1290°F (700°C) or parts of are permanently exposed to a temperature below 1290°F (700°C), Alloy 800H should be utilized. The high temperature resistance of Alloy 800HT is comparable to Alloy 800H. It also remains stable in long term high temperature service. Alloys 800H and 800AT are easily welded and processed by standard shop fabrication practices.
Applications
- Chemical and Petrochemical Processing - process equipment for the production of ethylene, ethylene dichloride, acetic anhydride, ketene, nitric acid and oxy-alcohol
- Petroleum Refining - steam/hydrocarbon reformers and hydrodealkylation units
- Power Generation - steam super-heaters and high temperature heat exchangers in gas-cooled nuclear reactors, heat exchangers and piping systems in coal-fired power plants
- Thermal Processing Fixtures - radiant tubes, muffles, retorts and fixtures for heat-treating furnaces
一般属性
使用 Prospector 建立免費帳戶時,可造訪 Sandmeyer Nickel Alloy 800HT 的完整資料表詳細資訊。您將找到有關物理、機械和硬度規格的完整資訊
Technical Datasheet (English)
下载文档加工
Find specific processing information for Sandmeyer Nickel as well as general information for the Nickel - Wrought - Ni-Fe-Cr Alloy generic family. 注册 或 登录 了解更多信息。
购买地点
您可以從 1 個經銷商或製造商處購買 Sandmeyer Nickel Alloy 800HT。 注册 或 登录 了解更多信息。