Harris 0 is an economical alloy designed for brazing copper to copper connections. This alloy flows quickly at brazing temperature so requires close joint tolerance, less than 0.005". Is a frequent choice for copper brazing.

Harris 0 is also a suitable choice for brazing brass. In this application operators should take care to avoid over heating the brass and use Harris Stay Silv ® white brazing flux.

Harris 0 is not recommended for brazing steel or other ferrous base metals. The phosphorus content will form a low ductility intermetallic with the base metal.

CORROSION RESISTANCE
Generally similar to the copper base metal, but phosphorus containing alloys, including Harris 0, should not be used if the braze is exposed to sulfur or sulfur compounds in service.

AVAILABLE FORMS
Standard wire diameters in coils and rod Preform rings, Strip. Shims

RECOMMENDED FLUX:
No flux is required for copper brazing. For brazing brass or copper to brass, use Stay-Silv ® white flux.