Heat Resisting Austenitic Stainless Steel U-310S Si-1.4841
U-309S-1.4833 has very good oxidation resistance and this is improved even further with U-309S Si- 1.4828 , which has a higher silicon content.
The U-309S types have a lower nickel content compared to the U-310S types and this improves their resistance to hydrogen sulphide (H2S) attack at high temperatures.
The U-309S types are low carbon grades and are recommended for applications where sensitisation and subsequent corrosion by high temperature gasses or condensates during shutdown may pose a problem.
The U-309S types are used, for example, in applications such as furnace parts, fire box sheets, high temperature containers, catalytic converters, exhaust systems, etc.
The U-310S types have higher chromium and nickel contents to enable them to resist oxidation in continuous service at temperatures up to 1 200°C provided reducing sulphur gases are not present.
The higher silicon content in U-310S Si-1.4841 improves this oxidiation resistance even further.
In intermittent high temperature service, the U-310S types can be used at temperatures up to 1 030°C as they resist scaling and have a relatively low coefficient of expansion differential between the metal and the scale. These stainless steels have superior resistance to both the U-304 types and the U-309S types in carburising and reducing environments.
The U-310S types are used in applications such as furnace parts, muffles, radiant tubes, ammonia converters, etc.
一般属性
使用 Prospector 建立免費帳戶時,可造訪 Heat Resisting Austenitic Stainless Steel U-310S Si-1.4841 的完整資料表詳細資訊。您將找到有關物理、機械和硬度規格的完整資訊
Technical Datasheet (English)
下载文档加工
Find specific processing information for Heat Resisting Austenitic Stainless Steel as well as general information for the Steel - Wrought - Stainless - Austenitic generic family. 注册 或 登录 了解更多信息。
购买地点
您可以從 1 個經銷商或製造商處購買 Heat Resisting Austenitic Stainless Steel U-310S Si-1.4841。 注册 或 登录 了解更多信息。