HARRIS® 0
Harris 0 is also a suitable choice for brazing brass. In this application operators should take care to avoid over heating the brass and use Harris Stay Silv ® white brazing flux.
Harris 0 is not recommended for brazing steel or other ferrous base metals. The phosphorus content will form a low ductility intermetallic with the base metal.
CORROSION RESISTANCE
Generally similar to the copper base metal, but phosphorus containing alloys, including Harris 0, should not be used if the braze is exposed to sulfur or sulfur compounds in service.
AVAILABLE FORMS
Standard wire diameters in coils and rod Preform rings, Strip. Shims
RECOMMENDED FLUX:
No flux is required for copper brazing. For brazing brass or copper to brass, use Stay-Silv ® white flux.
Propriedades gerais
Acesse os detalhes completos da ficha de dados de HARRIS® 0 quando você criar sua conta gratuita no Prospector. Você encontrará informações completas sobre especificações físicas, mecânicas e de dureza
Technical Datasheet (English)
Baixar o documentoProcessamento
Encontre informações de processamento específicas para HARRIS®, além de informações gerais para a família genérica Copper - Wrought - Cu-P Alloy. Inscreva-se ou Faça login para mais informações.
Onde comprar
Você pode adquirir HARRIS® 0 de 1 distribuidores ou fabricantes. Inscreva-se ou Faça login para mais informações.
PROSPECTOR
Encontre soluções, não somente materiais.
Quando se junta ao Prospector, você se beneficia de recursos e ferramentas dinâmicas para encontrar soluções rapidamente..
Inscreva-se hoje mesmo