Cr-Mn-Ni Austenitic Stainless Steel U-304H

Família genérica: Steel - Wrought - Stainless - AusteniticFornecido por: Columbus Stainless (Pty) Ltd
The Cr-(Mn)-Ni austenitics are the most versatile and widely used of all the stainless steels. Their chemical composition, mechanical properties, weldability and corrosion/oxidation resistance provide the best all-round performance stainless steels at relatively low cost. They have excellent low temperature properties and respond well to hardening by cold working.

The carefully controlled chemical composition of the Cr-(Mn)-Ni austenitics enables them to be deep drawn without intermediate annealing. This has made them dominant in the manufacture of drawn stainless steel parts such as sinks and saucepans. They are readily press-braked or roll formed into a variety of shapes for applications in the industrial, architectural and transportation fields.

U-202 is a lower cost alternative to the Cr-Ni austenitic stainless steels, such as U-304. About half the nickel of U-304 is replaced with alloy additions of manganese and nitrogen. Copper is added to compensate for the increased work hardening rate, caused by the nitrogen additions.

U-202 thus has very similar mechanical properties to U-304 and has excellent ductility and formability. It also has excellent low temperature properties and responds similarly to U-304DQ in drawing operations. U-202 has good welding characteristics. Post weld annealing is not normally required. The pitting resistance of U-202 is not as good as the U-304 types and is similar to U-430.

The low carbon grades (U-304L-ASTM, U-304L-ASME and U- 304LDDQ) do not require post weld annealing and find extensive use in heavy gauge components where freedom from carbide precipitation is often required.

The high carbon grades (U-304, U-304H, U-304DQ and U-304DDQ) have good welding characteristics. There is, however, a risk of carbide precipitation and sensitisation with a possible concomitant loss in intergranular corrosion resistance in corrosive environments in thicker gauges. Post weld annealing is not normally required to restore the excellent performance of these grades in a wide range of corrosive conditions.

U-304H, with a higher carbon content, is normally specified where good mechanical properties at elevated temperatures are required. These grades also have a larger grain sizes (ASTM 7 or coarser) to improve the high temperature creep resistance.

The drawing quality (U-304DQ) and deep drawing quality (U- 304DDQ and U-304LDDQ) grades have increased levels of nickel to improve their formability and are thus used in forming opera - tions where the depth of the formed part exceeds the diameter.

U-304LS has a high sulphur level, although still within the U-304L specification. This is to improve the machinability, weldability and forgeability. U-304LS should not be confused with the free-ma - chining grades that have much higher levels of sulphur.

U-304LN has a higher nitrogen content to improve the strength and is also particularly suitable for cryogenic applications. U-321 is a titanium stabilised version of U-304 and is used in applications exposed to the temperature range 450°C to 850°C where there is a high risk of sensitisation.

U-321 has higher elevated temperature properties than U-304. Although having good resistance to oxidation and sensitisation, CS321 is unsuitable for use in highly oxidis - ing environments due to possible ‘knifeline' attack. Typical applications for CS321 would include furnace parts, after burners, expansion bellows, compensators, catalytic converters, etc.
Propriedades gerais

Acesse os detalhes completos da ficha de dados de Cr-Mn-Ni Austenitic Stainless Steel U-304H quando você criar sua conta gratuita no Prospector. Você encontrará informações completas sobre especificações físicas, mecânicas e de dureza

Status do material
Comercial: Ativo
Documentos
description

Technical Datasheet (English)

Baixar o documento
Disponibilidade
África & Oriente Médio
Outras propriedades
Applicable Specifications, Metal Type, Alloy Identification, Type Analysis, Densidade, Tensile Strength (Ultimate), Tensile Strength (Yield), 0.2%, Tensile Elongation (Break), Módulo de Tensão, Mean Specific Heat, Mean CTE, Condutividade térmica, Electrical Resistivity
Access 13 properties in Metals. Create your free account or sign into Prospector.
Processamento

Encontre informações de processamento específicas para Cr-Mn-Ni Austenitic Stainless Steel, além de informações gerais para a família genérica Steel - Wrought - Stainless - Austenitic. Inscreva-se ou Faça login para mais informações.

Onde comprar

Você pode adquirir Cr-Mn-Ni Austenitic Stainless Steel U-304H de 1 distribuidores ou fabricantes. Inscreva-se ou Faça login para mais informações.

Login/registro no Prospector
Características Premium

PROSPECTOR

Encontre soluções, não somente materiais.

Quando se junta ao Prospector, você se beneficia de recursos e ferramentas dinâmicas para encontrar soluções rapidamente..

Inscreva-se hoje mesmo