RA 6Al-4V ELI
Low interstitial version of Ti-6Al-4V, for maximum toughness. Preferred for marine and cryogenic applications. This grade is normally used in the annealed condition. Ti-6Al-4V is the preferred choice for the medical implant field.
Stress relief 900-1200°F 1 to 4 hours, air cool. Duplex anneal, bar and forgings: Solution anneal 50-100°F below the beta transus, hold 1 hour minimum, air cool. Then reheat within the range 1300-1400°F, hold 1 hour minimum, air cool. Stress - relief annealing is performed after welding.
Stress relief 900-1200°F 1 to 4 hours, air cool. Duplex anneal, bar and forgings: Solution anneal 50-100°F below the beta transus, hold 1 hour minimum, air cool. Then reheat within the range 1300-1400°F, hold 1 hour minimum, air cool. Stress - relief annealing is performed after welding.
一般属性
使用 Prospector 建立免費帳戶時，可造訪 RA 6Al-4V ELI 的完整資料表詳細資訊。您將找到有關物理、機械和硬度規格的完整資訊
物料形态
已商用：当前有效
文档
description
Technical Datasheet (English)
下载文档可用性
北美洲, 欧洲, 亚太地区
其他属性
Applicable Specifications, Metal Type, Alloy Identification, Type Analysis, 密度, Tensile Strength (Ultimate), Tensile Strength (Yield), 0.2%, Tensile Elongation (Break), Reduction of Area, Mean CTE
加工
Find specific processing information for RA as well as general information for the Titanium - Wrought - Alpha-Beta Alloy generic family. 注册 或 登录 了解更多信息。
购买地点
Prospector 登录/注册