ATI Steel ATI 17-4™
The S17400 alloy is martensitic in structure in the annealed condition and is further strengthened by a low temperature treatment which precipitates a copper containing phase in the alloy. In comparison to many alloys in the precipitation hardening family, the S17400 alloy requires a simple heat treatment; a one step process conducted at a temperature in the range 900°F (482°C) to 1150°F (621°C) depending on the combination of strength and toughness desired. A wide range of properties can be produced by this one step heat treatment. Heat treatment in the 900°F (482°C) range produces highest strength, although slightly less than that of alloys like S17700 or S15700. The latter precipitation hardening stainless steels generally require more steps to complete heat treatment.
一般属性
使用 Prospector 建立免費帳戶時,可造訪 ATI Steel ATI 17-4™ 的完整資料表詳細資訊。您將找到有關物理、機械和硬度規格的完整資訊
Technical Datasheet (English)
下载文档加工
Find specific processing information for ATI Steel as well as general information for the Steel - Wrought - Stainless - Precipitation Hardening generic family. 注册 或 登录 了解更多信息。