Stainless Steel 410 Cb
The alloy offers three major advantages over Type 410:
- Greater ease in heat treating
- Higher strength and toughness
- Improved grain size control
When tempering Type 410, rapid changes in hardness can occur with relatively minor changes in time and temperature. For this reason, it is often difficult to obtain uniform, consistent hardness from part to part, especially when heat treating large furnace loads where temperature variations are more likely to exist. AK Steel 410 Cb alleviates that problem because it is not as sensitive to time and temperature variations. Specific hardness ranges can be maintained more consistently.
In the annealed condition, the mechanical properties of AK Steel 410 Cb are about the same as those of Type 410. However, after tempering, the alloy has appreciably higher strength and ductility than Type 410 at both elevated and sub-zero temperatures. Also, the impact strength of AK Steel 410 Cb is significantly higher than Type 410 in most heat-treated conditions.
AK Steel 410 Cb can replace 409 Ni in some flange applications. In addition, it can be used as a replacement wherever Type 410 is specified. In a wide variety of applications that could include exhaust flanges, steam turbine blades, aerospace equipment and flat springs.
一般属性
使用 Prospector 建立免費帳戶時,可造訪 Stainless Steel 410 Cb 的完整資料表詳細資訊。您將找到有關物理、機械和硬度規格的完整資訊
Technical Datasheet (English)
下载文档加工
Find specific processing information for Stainless Steel as well as general information for the Steel - Wrought - Stainless - Martensitic generic family. 注册 或 登录 了解更多信息。