For maximum strength: solution-treated and aged (STA) condition is: For sheet, 1675-1725°F 5 to 25 minutes, water quench. Age 975°F 4 to 6 hours, air cool. For bars and forgings, 1650-1775°F 1 hour, water quench. Age 900-1150°F 4 to 8 hours, air cool.
Ti 6Al-4V is resistant to general corrosion but may be quickly attacked by environments that cause breakdown of the protective oxide. These include hydrofluoric (HF), hydrochloric (HCl), sulfuric and phosphoric acids. Inhibitors may help for the last three but not for HF. Ti 6Al-4V resists attack by pure hydrocarbons, and most chlorinated and fluorinated hydrocarbons (provided water has not caused formation of small amounts of HCl and HF).
Ti 6Al-4V is susceptible to chloride stress corrosion cracking (SCC), although being among the better of the titanium alloys in this regard. For marine environments silver plated bolts are not used, as silver bonds easily with chlorine in this environment. Ti 6Al-4V is also susceptible to SCC in environments such as methyl alcohol, red fuming HNO3, and N2O4. In the case of red fuming nitric acid, the problem is limited to environments containing less than 1.5% water, or more than 6% NO2. Failure in N2O4 has occurred when oxygen and chlorides were present as impurities.
一般的な属性
Prospectorで無料のアカウントを作成し、RA 6Al-4V STAのデータシート詳細すべてにアクセスします。そこで、物理、機械、硬度仕様に関するすべての情報をご覧ください
Technical Datasheet (English)
ドキュメントのダウンロード加工
RAの具体的な加工情報や、Titanium - Wrought - Alpha-Beta Alloyジェネリックファミリーの一般情報をご確認いただけます。 登録 または サインイン 詳細情報を確認してください。
ご購入方法
1の販売業者や製造者からRA 6Al-4V STAを購入できます。 登録 または サインイン 詳細情報を確認してください。
PROSPECTOR
材料だけでなく、ソリューションも見つけることができます。
Prospectorにご登録いただくと、ダイナミックなツールおよび機能を活用して、迅速にソリューションを見つけることができます。
今すぐご登録ください