Low interstitial version of Ti-6Al-4V, for maximum toughness. Preferred for marine and cryogenic applications. This grade is normally used in the annealed condition. Ti-6Al-4V is the preferred choice for the medical implant field.
Stress relief 900-1200°F 1 to 4 hours, air cool. Duplex anneal, bar and forgings: Solution anneal 50-100°F below the beta transus, hold 1 hour minimum, air cool. Then reheat within the range 1300-1400°F, hold 1 hour minimum, air cool. Stress - relief annealing is performed after welding.
Stress relief 900-1200°F 1 to 4 hours, air cool. Duplex anneal, bar and forgings: Solution anneal 50-100°F below the beta transus, hold 1 hour minimum, air cool. Then reheat within the range 1300-1400°F, hold 1 hour minimum, air cool. Stress - relief annealing is performed after welding.
一般的な属性
Prospectorで無料のアカウントを作成し、RA 6Al-4V ELIのデータシート詳細すべてにアクセスします。そこで、物理、機械、硬度仕様に関するすべての情報をご覧ください
材料ステータス
供給可能
ドキュメント
description
Technical Datasheet (English)
ドキュメントのダウンロード可用性
アジア太平洋地域, 欧州, 北アメリカ
その他の属性
Applicable Specifications, Metal Type, Alloy Identification, Type Analysis, 密度, Tensile Strength (Ultimate), Tensile Strength (Yield), 0.2%, Tensile Elongation (Break), Reduction of Area, Mean CTE
加工
RAの具体的な加工情報や、Titanium - Wrought - Alpha-Beta Alloyジェネリックファミリーの一般情報をご確認いただけます。 登録 または サインイン 詳細情報を確認してください。
ご購入方法
1の販売業者や製造者からRA 6Al-4V ELIを購入できます。 登録 または サインイン 詳細情報を確認してください。
Prospectorのログイン/登録
プレミアム機能
PROSPECTOR
材料だけでなく、ソリューションも見つけることができます。
Prospectorにご登録いただくと、ダイナミックなツールおよび機能を活用して、迅速にソリューションを見つけることができます。
今すぐご登録ください