Eastern Alloys, Inc. Slush Casting Alloys
In the slush casting process, metal is poured into a slush-casting mold, allowed time to solidify along the mold wall only, and then poured out. The resulting "hollow" casting is then ejected and cooled. Its primary use is for decorative castings not subjected to high stress conditions, such as lamp bases.
Because of the low melting temperatures and excellent fluidity, the alloy should be cast at temperatures not to exceed 825°F. Since the alloy is normally melted and held in cast iron kettles, high temperatures will cause excessive iron pickup, resulting in poor castability and poor finishing characteristics.
Since the alloy contains no Magnesium (to ensure high fluidity) extreme care must be taken to prevent contamination by Pb (lead), Sn (tin) or Cd (cadmium) which can cause subsequent inter-granular corrosion. Castings are normally plated soon after finishing to preclude any oxidation or corrosion problems.
一般的な属性
Prospectorで無料のアカウントを作成し、Eastern Alloys, Inc. Slush Casting Alloysのデータシート詳細すべてにアクセスします。そこで、物理、機械、硬度仕様に関するすべての情報をご覧ください
Technical Datasheet (English)
ドキュメントのダウンロード加工
Eastern Alloys, Inc.の具体的な加工情報や、Zinc - Cast - Alloyジェネリックファミリーの一般情報をご確認いただけます。 登録 または サインイン 詳細情報を確認してください。
ご購入方法
1の販売業者や製造者からEastern Alloys, Inc. Slush Casting Alloysを購入できます。 登録 または サインイン 詳細情報を確認してください。
PROSPECTOR
材料だけでなく、ソリューションも見つけることができます。
Prospectorにご登録いただくと、ダイナミックなツールおよび機能を活用して、迅速にソリューションを見つけることができます。
今すぐご登録ください