RA 446
446 has a high ductile-to-brittle impact transition temperature. Therefore, successful forming and bending is aided by low forming speeds, edge preparation and preheating to 250-400°F. Annealing, when necessary should be performed at 1550-1650°F followed by rapid cool.
Welding may be accomplished by conventional methods. Preheating and postheating to 300-600°F is helpful. Austenitic weld fillers, such as AWS E310 or E312 are generally suggested to maximize weld deposit ductility.
Propriétés générales
Consultez la fiche technique complète de RA 446 en créant gratuitement votre compte Prospector. Vous y trouverez des informations exhaustives sur les propriétés physiques et mécaniques et sur la dureté
Technical Datasheet (English)
Télécharger le documentTraitement en cours
Find specific processing information for RA as well as general information for the Steel - Wrought - Stainless - Ferritic generic family. S’inscrire ou Connexion pour en savoir plus.
Où acheter
Vous pouvez acheter RA 446 auprès de 1 distributeurs ou fabricants. S’inscrire ou Connexion pour en savoir plus.
PROSPECTOR
Trouvez des solutions, pas seulement des matériaux..
Avec Prospector, vous disposez d’outils et de fonctions dynamiques qui vous permettront de trouver des solutions au plus vite.
S’inscrire aujourd’hui