High Temp Metals HAYNES 188
Alloy 188 has average room temperature tensile properties in the bright annealed condition of 137.2 ksi (946 MPa) ultimate strength, 67.3 ksi (464 MPa) yield strength and 53% elongation. At 1800°F (980°C) the alloy has ultimate and yield strengths of 35.2 ksi (243 MPa) and 19.0 ksi (131 MPa), respectively, with 59% elongation. Cryogenic temperatures do not significantly affect the ductility of alloy 188, but strength levels are increased markedly.
The excellent oxidation resistance of Haynes 188 results from minute additions of lanthanum, which modifies the protective oxide scale in such a manner that the oxide becomes extremely tenacious and retards diffusion when exposed to temperatures through 2100°F (1150°C).
Haynes 188 exhibits good ductility after prolonged exposure at temperatures of 1200, 1400, and 1600°F (650, 760 and 870°C) for 16,000 hours.
General Properties
Access the complete datasheet details for High Temp Metals HAYNES 188 when you create your free account with Prospector. You’ll find complete information on physical, mechanical and hardness specs.
Technical Datasheet (English)
Download DocumentProcessing
Find specific processing information for High Temp Metals as well as general information for the Cobalt - Wrought - Alloy generic family. Register or Sign In for more information.
Where To Buy
You can purchase High Temp Metals HAYNES 188 from 1 distributors or manufacturers. Register or Sign In for more information.
PROSPECTOR
Find solutions, not just materials.
When you join Prospector, you leverage the dynamic tools and features to find solutions fast.
Register Today