  • Cr-Mn-Ni Austenitic Stainless Steel U-304DQ

Cr-Mn-Ni Austenitic Stainless Steel U-304DQ

ジェネリックファミリー: Steel - Wrought - Stainless - Austenitic提供元: Columbus Stainless (Pty) Ltd
The Cr-(Mn)-Ni austenitics are the most versatile and widely used of all the stainless steels. Their chemical composition, mechanical properties, weldability and corrosion/oxidation resistance provide the best all-round performance stainless steels at relatively low cost. They have excellent low temperature properties and respond well to hardening by cold working.

The carefully controlled chemical composition of the Cr-(Mn)-Ni austenitics enables them to be deep drawn without intermediate annealing. This has made them dominant in the manufacture of drawn stainless steel parts such as sinks and saucepans. They are readily press-braked or roll formed into a variety of shapes for applications in the industrial, architectural and transportation fields.

U-202 is a lower cost alternative to the Cr-Ni austenitic stainless steels, such as U-304. About half the nickel of U-304 is replaced with alloy additions of manganese and nitrogen. Copper is added to compensate for the increased work hardening rate, caused by the nitrogen additions.

U-202 thus has very similar mechanical properties to U-304 and has excellent ductility and formability. It also has excellent low temperature properties and responds similarly to U-304DQ in drawing operations. U-202 has good welding characteristics. Post weld annealing is not normally required. The pitting resistance of U-202 is not as good as the U-304 types and is similar to U-430.

The low carbon grades (U-304L-ASTM, U-304L-ASME and U- 304LDDQ) do not require post weld annealing and find extensive use in heavy gauge components where freedom from carbide precipitation is often required.

The high carbon grades (U-304, U-304H, U-304DQ and U-304DDQ) have good welding characteristics. There is, however, a risk of carbide precipitation and sensitisation with a possible concomitant loss in intergranular corrosion resistance in corrosive environments in thicker gauges. Post weld annealing is not normally required to restore the excellent performance of these grades in a wide range of corrosive conditions.

U-304H, with a higher carbon content, is normally specified where good mechanical properties at elevated temperatures are required. These grades also have a larger grain sizes (ASTM 7 or coarser) to improve the high temperature creep resistance.

The drawing quality (U-304DQ) and deep drawing quality (U- 304DDQ and U-304LDDQ) grades have increased levels of nickel to improve their formability and are thus used in forming opera - tions where the depth of the formed part exceeds the diameter.

U-304LS has a high sulphur level, although still within the U-304L specification. This is to improve the machinability, weldability and forgeability. U-304LS should not be confused with the free-ma - chining grades that have much higher levels of sulphur.

U-304LN has a higher nitrogen content to improve the strength and is also particularly suitable for cryogenic applications. U-321 is a titanium stabilised version of U-304 and is used in applications exposed to the temperature range 450°C to 850°C where there is a high risk of sensitisation.

U-321 has higher elevated temperature properties than U-304. Although having good resistance to oxidation and sensitisation, CS321 is unsuitable for use in highly oxidis - ing environments due to possible ‘knifeline' attack. Typical applications for CS321 would include furnace parts, after burners, expansion bellows, compensators, catalytic converters, etc.
一般的な属性

Prospectorで無料のアカウントを作成し、Cr-Mn-Ni Austenitic Stainless Steel U-304DQのデータシート詳細すべてにアクセスします。そこで、物理、機械、硬度仕様に関するすべての情報をご覧ください

材料ステータス
供給可能
ドキュメント
description

Technical Datasheet (English)

ドキュメントのダウンロード
可用性
アフリカ&中東
その他の属性
Applicable Specifications, Metal Type, Alloy Identification, Type Analysis, 密度, Tensile Strength (Ultimate), Tensile Strength (Yield), 0.2%, Tensile Elongation (Break), 引張係数, Mean Specific Heat, Mean CTE, 熱伝導性, Electrical Resistivity
Access 13 properties in Metals. Create your free account or sign into Prospector.
加工

Cr-Mn-Ni Austenitic Stainless Steelの具体的な加工情報や、Steel - Wrought - Stainless - Austeniticジェネリックファミリーの一般情報をご確認いただけます。 登録 または サインイン 詳細情報を確認してください。

ご購入方法

1の販売業者や製造者からCr-Mn-Ni Austenitic Stainless Steel U-304DQを購入できます。 登録 または サインイン 詳細情報を確認してください。

Prospectorのログイン/登録
プレミアム機能

PROSPECTOR

材料だけでなく、ソリューションも見つけることができます。

Prospectorにご登録いただくと、ダイナミックなツールおよび機能を活用して、迅速にソリューションを見つけることができます。

今すぐご登録ください