HARRIS® 0

Famille générique : Copper - Wrought - Cu-P Alloy • Documents mis à disposition par : THE HARRIS PRODUCTS GROUP

Harris 0 is an economical alloy designed for brazing copper to copper connections. This alloy flows quickly at brazing temperature so requires close joint tolerance, less than 0.005". Is a frequent choice for copper brazing.

Harris 0 is also a suitable choice for brazing brass. In this application operators should take care to avoid over heating the brass and use Harris Stay Silv ® white brazing flux.

Harris 0 is not recommended for brazing steel or other ferrous base metals. The phosphorus content will form a low ductility intermetallic with the base metal.

CORROSION RESISTANCE
Generally similar to the copper base metal, but phosphorus containing alloys, including Harris 0, should not be used if the braze is exposed to sulfur or sulfur compounds in service.

AVAILABLE FORMS
Standard wire diameters in coils and rod Preform rings, Strip. Shims

RECOMMENDED FLUX:
No flux is required for copper brazing. For brazing brass or copper to brass, use Stay-Silv ® white flux.

Propriétés générales

Consultez la fiche technique complète de HARRIS® 0 en créant gratuitement votre compte Prospector. Vous y trouverez des informations exhaustives sur les propriétés physiques et mécaniques et sur la dureté

État du matériau

Commercial : actif

Documents

Technical Datasheet (English)

Télécharger le document

Disponibilité

Amérique du Nord

Autres propriétés

Applicable Specifications, Forms Available, Metal Type, Type Analysis, Electrical Resistivity, Electrical Conductivity

Access 6 properties in Metals. Create your free account or sign into Prospector.

Traitement en cours

Find specific processing information for HARRIS® as well as general information for the Copper - Wrought - Cu-P Alloy generic family. S’inscrire ou Connexion pour en savoir plus.