High Temp Metals HAYNES 188
Alloy 188 has average room temperature tensile properties in the bright annealed condition of 137.2 ksi (946 MPa) ultimate strength, 67.3 ksi (464 MPa) yield strength and 53% elongation. At 1800°F (980°C) the alloy has ultimate and yield strengths of 35.2 ksi (243 MPa) and 19.0 ksi (131 MPa), respectively, with 59% elongation. Cryogenic temperatures do not significantly affect the ductility of alloy 188, but strength levels are increased markedly.
The excellent oxidation resistance of Haynes 188 results from minute additions of lanthanum, which modifies the protective oxide scale in such a manner that the oxide becomes extremely tenacious and retards diffusion when exposed to temperatures through 2100°F (1150°C).
Haynes 188 exhibits good ductility after prolonged exposure at temperatures of 1200, 1400, and 1600°F (650, 760 and 870°C) for 16,000 hours.
Propiedades generales
Acceda a los detalles completos de la hoja de datos de High Temp Metals HAYNES 188 cuando cree su cuenta gratuita con Prospector. Encontrará información completa sobre especificaciones físicas, mecánicas y de dureza
Technical Datasheet (English)
Descargar documentoProcesando
Encuentre información de procesamiento específica para High Temp Metals, así como información general para la familia genérica de Cobalt - Wrought - Alloy. Registrarse o Iniciar sesión para obtener más información.
Dónde comprar
Puede comprar High Temp Metals HAYNES 188 de 1 distribuidores o fabricantes. Registrarse o Iniciar sesión para obtener más información.
PROSPECTOR
Encuentre soluciones, no solo materiales.
Cuando se une a Prospector, aprovecha las herramientas y funciones dinámicas para encontrar soluciones rápidamente.
Regístrese hoy