HARRIS® 0HP
brazing copper return bends in HVACR evaporator and condenser coils.
Harris 0HP is also a suitable choice for brazing brass. In this application operators should take care to avoid over heating the brass and use Harris Stay Silv ® white brazing flux.
Harris 0HP is not recommended for brazing steel or other ferrous base metals. The phosphorus content will form a low ductility intermetallic with the base metal.
CORROSION RESISTANCE
Generally similar to the copper base metal, but phosphorus containing alloys, including Harris 0HP, should not be used if the braze is exposed to sulfur or sulfur compounds in service.
AVAILABLE FORMS
Standard wire diameters in coils, rod and preform rings.
RECOMMENDED FLUX:
No flux is required for copper brazing. For brazing brass or copper to brass, use Stay-Silv ® white flux.
Allgemeine Eigenschaften
Richten Sie ein kostenloses Prospector-Konto ein, um Zugang zu sämtlichen Angaben des Produktdatenblatts von HARRIS® 0HP zu erhalten. Dort finden Sie alle Angaben zu den physikalischen, mechanischen und Härteeigenschaften
Technical Datasheet (English)
Dokument herunterladenVerarbeitung
Finden Sie bestimmte Informationen zur Verarbeitung für HARRIS® sowie allgemeine Informationen zum allgemeinen Produktkreis Copper - Wrought - Cu-P Alloy. Registrieren oder Anmelden um mehr Informationen erhalten.
Bezugsquellen
Sie können HARRIS® 0HP von 1 Händler(n) oder Hersteller(n) kaufen. Registrieren oder Anmelden um mehr Informationen erhalten.
PROSPECTOR
Finden Sie Lösungen, nicht nur Materialien.
Wenn Sie sich bei Prospector registrieren, können Sie unsere dynamischen Werkzeuge und Funktionen nutzen, um schnell Lösungen zu finden.
Noch heute registrieren