Heat Resisting Austenitic Stainless Steel U-310S-1.4845 Datenblatt

Wrought Stainless Steel

Geliefert von Columbus Stainless (Pty) Ltd

Create your free Prospector account to view this complete product datasheet. A free account includes access to hundreds of thousands of detailed technical datasheets. Erstellen Sie Ihr kostenloses Konto
Produktbeschreibung
The heat resisting austenitics are highly alloyed stainless steel used for their excellent oxidation resistance, high temperature strength and creep resistance in high temperature applications. They are tough and ductile and can be readily fabricated and machined.

U-309S-1.4833 has very good oxidation resistance and this is improved even further with U-309S Si- 1.4828 , which has a higher silicon content.

The U-309S types have a lower nickel content compared to the U-310S types and this improves their resistance to hydrogen sulphide (H2S) attack at high temperatures.

The U-309S types are low carbon grades and are recommended for applications where sensitisation and subsequent corrosion by high temperature gasses or condensates during shutdown may pose a problem.

The U-309S types are used, for example, in applications such as furnace parts, fire box sheets, high temperature containers, catalytic converters, exhaust systems, etc.

The U-310S types have higher chromium and nickel contents to enable them to resist oxidation in continuous service at temperatures up to 1 200°C provided reducing sulphur gases are not present.

The higher silicon content in U-310S Si-1.4841 improves this oxidiation resistance even further.

In intermittent high temperature service, the U-310S types can be used at temperatures up to 1 030°C as they resist scaling and have a relatively low coefficient of expansion differential between the metal and the scale. These stainless steels have superior resistance to both the U-304 types and the U-309S types in carburising and reducing environments.

The U-310S types are used in applications such as furnace parts, muffles, radiant tubes, ammonia converters, etc.
Allgemein  
Materialstatus 
  • Kommerziell: Aktiv
Verfügbarkeit 
  • Afrika und Mittlerer Osten
Available Documents
Technical Datasheet (English)
Metals General
Nominalwert
Einheit
 
Applicable Specifications
     
--
 
 
-- 2
 
 
-- 3
 
 
-- 4
 
 
Metal Type
 
 
Alloy Identification
 
 
Metals Type Analysis
Nominalwert
Einheit
 
Type Analysis
     
Carbon
%
 
Chromium
%
 
Manganese
%
 
Nickel
%
 
Nitrogen
%
 
Phosphorus
%
 
Silicon
%
 
Sulfur
%
 
Metals Physical
Nominalwert
Einheit
 
Dichte
lb/in³
 
Metals Mechanical
Nominalwert
Einheit
 
Tensile Strength (Ultimate)
     
1022°F 5
ksi
 
1022°F 6
ksi
 
Tensile Strength (Yield), 0.2%
     
1022°F 7
ksi
 
1022°F 8
ksi
 
Tensile Elongation (Break)
     
212°F
%
 
392°F
%
 
Zug-Modul
     
-- 9
ksi
 
-- 10
ksi
 
Metals Thermal
Nominalwert
Einheit
 
Mean Specific Heat
Btu/lb/°F
 
Mean CTE
     
32 bis 212°F
in/in/°F
 
32 bis 572°F
in/in/°F
 
Wärmeleitfähigkeit
     
212°F
Btu·in/hr/ft²/°F
 
932°F
Btu·in/hr/ft²/°F
 
Metals Electrical
Nominalwert
Einheit
 
Electrical Resistivity
ohms·cir·mil/ft
 
Anmerkungen
1Typische Eigenschaften, nicht als Spezifikationen anzusehen
2Cold Rolled and Hot Rolled
3Hot Rolled
4Cold Rolled
51,000 Hours
610,000 Hours
71% Strain, 10,000 Hours
81% Strain, 100,000 Hours
9In Tension
10In Torsion
 
UL und das UL-Logo sind Handelsmarken von UL LLC © 2021 Alle Rechte vorbehalten.
Die in diesem Datenblatt enthaltenen Informationen wurden von UL Prospector auf der Grundlage der Angaben des Herstellers des Materials zusammengestellt. UL Prospector setzt sich dafür ein, die Genauigkeit der Daten zu gewährleisten. UL Prospector haftet jedoch in keinem Fall für die Daten/Werte und empfiehlt dringend, sich diese bei der endgültigen Auswahl des Materials vom Hersteller bestätigen zu lassen.